Disperse fine equiaxed α-Al2O3 nanoparticles with narrow size distribution are important materials in nanotechnology and nanomaterials, but syntheses of disperse fine equiaxed α-Al2O3 nanoparticles usually result in fine γ-Al2O3 nanoparticles or large α-Al2O3 nanoparticles larger than 15 nm. α-Al2O3 has a higher surface energy than γ-Al2O3 and becomes thermodynamically not stable with respect t...

In this study, the phase transition characteristics of flame-synthesized γ-Al2O3 nanoparticles to α-Al2O3 have been investigated. The nanoparticles were synthesized by using a coflow hydrogen diffusion flame. The phase transition and particle characteristics of the Al2O3 nanoparticles were determined by examining the crystalline structure and the shape of the collected nanoparticles before and ...

The cytotoxicity of 13 and 22 nm aluminum oxide (Al2O3) nanoparticles was investigated in cultured human bronchoalveolar carcinoma-derived cells (A549) and compared with 20 nm CeO2 and 40 nm TiO2 nanoparticles as positive and negative control, respectively. Exposure to both Al2O3 nanoparticles for 24 h at 10 and 25mgmL 1 doses significantly decreased cell viability compared with control. Howeve...

In this study, γ-Al2O3 particles were dispersed in p-type Bi0.4Sb1.6Te3 through mechanical alloying to form γ-Al2O3/Bi0.4Sb1.6Te3 composite powders. The composite powders were consolidated using vacuum hot pressing to produce nanoand microstructured composites. Thermoelectric (TE) measurements indicated that adding an optimal amount of γ-Al2O3 nanoparticles improves the TE performance of the fa...

The thermal atomic layer etching (ALE) of Al2O3 can be performed using sequential and self-limiting reactions with trimethylaluminum (TMA) and hydrogen fluoride (HF) as the reactants. The atomic layer deposition (ALD) of AlF3 can also be accomplished using the same reactants. This paper examined the competition between Al2O3 ALE and AlF3 ALD using in situ Fourier transform infrared (FTIR) vibra...

We report a quantitative measurement of the pressure effect on melting point elevation of encapsulated nanoparticles without epitaxial interfaces. By means of in situ x-ray diffraction, a substantial melting point elevation of about 15 K in encapsulated Al nanoparticles in Al2O3 shells without epitaxial interfaces was observed. Meanwhile, a pressure buildup of about 0.25 GPa on the Al nanoparti...

Organolead trihalide perovskite solar cells based upon the co-deposition of a combined Al2O3-perovskite layer at T < 110 °C are presented. We report an average PCE = 7.2% on a non-sintered Al2O3 scaffold in devices that have been manufactured from a perovskite precursor containing 5 wt% Al2O3 nanoparticles.

Pd nanoparticles (PdNPs) stabilized by methyl cellulose (MC) were synthesized in an aqueous solution, which are monodispersed nanoparticles. PdNPs/α-Al2O3 catalyst was prepared with monodispersed PdNPs and showed better catalytic performance than Pd/α-Al2O3 catalyst prepared by the incipient wetness impregnation method using Pd(NO3)2 as a precursor. The catalysts were characterized by transmiss...

A series of N-heteroaryl formamides were efficiently synthesized from heteroarylamines and formic acid using Al2O3 nanoparticles as a heterogeneous catalyst under solvent-free conditions. The smaller size of Al2O3 nanoparticles with a higher surface to volume ratio has a promising catalytic activity, resulting in a short reaction times and high reaction yields under mild reaction conditions. Th...

In this study, the nanofluids are produced by dispersing Al2O3 nanoparticles in the H2O/CH3OH binary mixtures using an ultrasonic equipment. Solid Sodium Chlorides (NaCl) with a fixed mass fraction are dissolved in the binary mixture for CO2 absorption. The main objective of this paper is to measure the thermal conductivity of the Al2O3 nanofluids using the transient hot-wire method. The experi...